Effect of a CGO buffer layer on the performance of (La0.6Sr0.4)0.995Co0.2Fe0.8O3-ä cathode in YSZ-Based SOFC
- Jesús Peña Martínez
- David Marrero López
- Carlos Sánchez Bautista
- A.J. Dos Santos García
- J.C. Ruiz Morales
- Jesús Canales Vázquez
- Pedro Felipe Núñez Coello
ISSN: 0366-3175
Year of publication: 2010
Volume: 49
Issue: 1
Pages: 15-22
Type: Article
More publications in: Boletín de la Sociedad Española de Cerámica y Vidrio
Metrics
JCR (Journal Impact Factor)
- Year 2010
- Journal Impact Factor: 0.204
- Journal Impact Factor without self cites: 0.115
- Article influence score: 0.082
- Best Quartile: Q4
- Area: MATERIALS SCIENCE, CERAMICS Quartile: Q4 Rank in area: 20/25 (Ranking edition: SCIE)
SCImago Journal Rank
- Year 2010
- SJR Journal Impact: 0.227
- Best Quartile: Q2
- Area: Industrial and Manufacturing Engineering Quartile: Q2 Rank in area: 144/509
- Area: Mechanics of Materials Quartile: Q3 Rank in area: 223/428
- Area: Ceramics and Composites Quartile: Q3 Rank in area: 53/121
Abstract
Las propiedades electroquimicas de los electrodos (La0.6Sr0.4)0.995Co0.2Fe0.8O3-� (LSCF) y composites de LSCF con ceria dopada con gadolinio (CGO), respecto la reaccion de reduccion del oxigeno, fueron estudiadas mediante espectroscopia de impedancia usando una configuracion de celda simetrica, con circonia estabilizada con itria (YSZ) como electrolito y CGO como capa de proteccion entre el material de electrodo y electrolito. Los mejores valores de resistencia de polarizacion fueron obtenidos para el composite LSCF-CGO (60/40, % en peso) con valores comprendidos entre 0,07 y 0,4 �¶cm2 para el rango de temperaturas de 650-775oC. El efecto de la capa intermedia de CGO sobre la resistencia de polarizacion del electrodo LSCF y la resistencia en serie de la celda simetrica LSCF/YSZ fue tambien investigado. La compatibilidad quimica de LSCF, YSZ y CGO se ha estudiado mediante difraccion de rayos X.